528 manual mold silicone rubber
1.The 528# manual mold silicone rubber is a flowable liquid, and the quality has nothing to do with the coor, It consists of two component. Part A is a flowable liquid silicone rubber, part B is the cuing agent. Firstly. after you previous work of dealing with the original model. ake some liquid silicone rubber, add 2%~3% curing agent of the amount of silicon. and mix them evenly. Then after vacuuum~pumping the mixture. you can pour it into the mold frame. Th silicone mold will cured in 2~3 hours.
2. Manual mold silicone rubber Operations
a.The perfusion molding is an easy way to make molds, it’s slowly and evenly perfuse the mixed siilicon rubber into the square frame. After the cross linking reaction.
FAQs of the manual mold silicone.
1.How do deal with the bubles during the mixing process?
I depends on your practical situation. Firstly you can deal the ixture with a vacuumizer if you have one. If no such machine, you can reduce the mixing ratio of the hardener from 4% to 1%~2%. Then in the prior period of the reaction of the mixture will be slower. then the air in the mixture will exhaust by itself for a longer curing time to release the buble.
2.what should you do for imcomplete curing after the mold is finished?
Two causes lead to his problem: 1 Inexact mixing ratio, not to weigh following the standard; 2 The mixture of the silicone and catalyst is not mixed evenly. You should avoid this kind of problem, otherwise there will be a waste of silicone mold.
Contact information:
Sales: Jessica Wong
Email: hyja(at)szrl(dot)net
Office phone:86-755-89948013
Mobile: 86-13058100008
Skype:sales.szrl
Website:www(dot)sellsilicone(dot)com
2. Manual mold silicone rubber Operations
a.The perfusion molding is an easy way to make molds, it’s slowly and evenly perfuse the mixed siilicon rubber into the square frame. After the cross linking reaction.
FAQs of the manual mold silicone.
1.How do deal with the bubles during the mixing process?
I depends on your practical situation. Firstly you can deal the ixture with a vacuumizer if you have one. If no such machine, you can reduce the mixing ratio of the hardener from 4% to 1%~2%. Then in the prior period of the reaction of the mixture will be slower. then the air in the mixture will exhaust by itself for a longer curing time to release the buble.
2.what should you do for imcomplete curing after the mold is finished?
Two causes lead to his problem: 1 Inexact mixing ratio, not to weigh following the standard; 2 The mixture of the silicone and catalyst is not mixed evenly. You should avoid this kind of problem, otherwise there will be a waste of silicone mold.
Contact information:
Sales: Jessica Wong
Email: hyja(at)szrl(dot)net
Office phone:86-755-89948013
Mobile: 86-13058100008
Skype:sales.szrl
Website:www(dot)sellsilicone(dot)com
Certificate
- ISO9001:2000
Main Products
silicone rubber